Evaluation of shear bond strength of e-mineral trioxide aggregate and biodentine with glass ionomer cement: An in vitro study


Department of Conservative Dentistry and Endodontics, College of Dental Science and Hospital, Indore, Madhya Pradesh, India

Correspondence Address:
Dr. Shivangi Trivedi
F12, Jhoomer Ghat, Near Hotel Mashal, College of Dental Science and Hospital, Rau, Indore, Madhya Pradesh
India
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/endo.endo_17_22

Rights and Permissions

Aim: The aim of this study was to evaluate the shear bond strength of glass ionomer cement (GIC) with e-mineral trioxide aggregate (MTA) and Biodentine when placed immediately and after initial set. Materials and Methodology: Forty acrylic blocks with 2-mm height and 5-mm diameter central holes were prepared and randomly divided into two equal groups (n = 20). Group A (n = 20) and Group B (n = 20) were filled with E-MTA and Biodentine, respectively. These groups (n = 20) were further divided into two subgroups each; subgroup A1 (n = 10) and A2 (n = 10) were the placement of GIC immediately over freshly mixed e-MTA and after initial set e-MTA, respectively, subgroup B1 (n = 10) and B2 (n = 10) were the placement of GIC immediately over freshly mixed Biodentine and after initial set Biodentine, respectively. All the samples were later subjected to UTM for shear bond strength test. Results: The highest shear bond strength was recorded with subgroup B1 were the placement of GIC immediately over freshly mixed Biodentine, i. e., (18.72 MPa) and lowest with subgroup A2 placement of GIC after initial set MTA (5.96MPa). The shear bond strength of GIC condensed over freshly mixed e-MTA (subgroup A1) shows higher mean value then after initial set MTA (subgroup A2); however, SBS was highest in the placement of GIC immediately over freshly mixed Biodentine (subgroup B1). Conclusion: Within the limitation of this in vitro study, it can be concluded that freshly mixed Biodentine can be restored immediately with GIC.


[FULL TEXT] [PDF]*
Print this article     Email this article
 Next article
 Previous article
 Table of Contents

 Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
 Citation Manager
 Access Statistics
 Reader Comments
 Email Alert *
 Add to My List *
 * Requires registration (Free)
 

 Article Access Statistics
    Viewed166    
    Printed8    
    Emailed0    
    PDF Downloaded36    
    Comments [Add]    

Recommend this journal